The Al-rich region of the Al-Mn-Ni alloy system. Part I: Ternary phases at 750-950 degrees C
The Al-rich region of the Al-Mn-Ni alloy system. Part I: Ternary phases at 750-950 degrees C
Ternary phases in the Al-rich region of the Al-Mn-Ni alloy system were studied at 950, 850 and 750 degrees C. Two new ternary intermetallic compounds were revealed: the phi-phase (Al5Co2-type, hP26, P6(3)/mmc: a = 0.76632(16) and c = 0.78296(15) nm) and the kappa-phase (kappa-Al14.4Cr3.4Ni1.1-type,...
Saved in:
Personal Name(s): | Balanetskyy, S. |
---|---|
Meisterernst, G. / Feuerbacher, M. | |
Contributing Institute: |
Mikrostrukturforschung; PGI-5 |
Published in: | Journal of alloys and compounds, 509 (2011) S. 3787 - 3794 |
Imprint: |
Lausanne
Elsevier
2011
|
Physical Description: |
3787 - 3794 |
DOI: |
10.1016/j.jallcom.2010.10.185 |
Document Type: |
Journal Article |
Research Program: |
Grundlagen für zukünftige Informationstechnologien |
Series Title: |
Journal of Alloys and Compounds
509 |
Subject (ZB): | |
Publikationsportal JuSER |
Ternary phases in the Al-rich region of the Al-Mn-Ni alloy system were studied at 950, 850 and 750 degrees C. Two new ternary intermetallic compounds were revealed: the phi-phase (Al5Co2-type, hP26, P6(3)/mmc: a = 0.76632(16) and c = 0.78296(15) nm) and the kappa-phase (kappa-Al14.4Cr3.4Ni1.1-type, hP227, P6(3)/m: a = 1.7625(10) and c = 1.2516(10) nm). The formation of the O-phase (Pmmn; oP650; O-Al77Cr14Pd9-type; a = 2.3316(16), b = 1.2424(15) and c = 3.2648(14) nm) was confirmed and its chemical composition as well as thermodynamic stability was specified. (C) 2010 Elsevier B.V. All rights reserved. |