X-ray powder diffraction data for high-temperature Al4Re(Ni)
X-ray powder diffraction data for high-temperature Al4Re(Ni)
A monoclinic phase isostructural to Al4W wits revealed in Al-Ni-Re close to the Al-Re terminal. It is assumed to he a ternary extension of the high-temperature Al4Re phase usually transforming in binary alloys even by sharp quenching from the existence temperatures. The powder X-ray diffraction patt...
Saved in:
Personal Name(s): | Grushko, B. |
---|---|
Contributing Institute: |
Mikrostrukturforschung; IFF-8 |
Published in: | Powder diffraction, 24 (2009) S. 29 - 31 |
Imprint: |
Newtown Square, Pa.
JCPDS
2009
|
Physical Description: |
29 - 31 |
DOI: |
10.1154/1.3078052 |
Document Type: |
Journal Article |
Research Program: |
Grundlagen für zukünftige Informationstechnologien |
Series Title: |
Powder Diffraction
24 |
Subject (ZB): | |
Publikationsportal JuSER |
A monoclinic phase isostructural to Al4W wits revealed in Al-Ni-Re close to the Al-Re terminal. It is assumed to he a ternary extension of the high-temperature Al4Re phase usually transforming in binary alloys even by sharp quenching from the existence temperatures. The powder X-ray diffraction pattern of this phase of the Al77Ni2.5Re20.5 composition was indexed for the Cm space group with a=5.1538(12) angstrom, b=17.410(5) angstrom, c=5.1546(15) angstrom, and beta= 100.548(16)degrees.(C) 2009 International Centre for Diffraction Data. [DOI: 10.1154/1.3078052] |