Nucleation and Growth Mechainsms of Zirconia Film Deposited on Porous Nickel Oxide - Zirconia Substrate by Electron Beam - Physical Vapor Deposition
Nucleation and Growth Mechainsms of Zirconia Film Deposited on Porous Nickel Oxide - Zirconia Substrate by Electron Beam - Physical Vapor Deposition
The structure of the transitional zone between a zirconia film deposited by EB-PVD and its porous NiO-ZrO2 substrate were studied using transmission and scanning electron microscopy. The plausible condensation mechanisms of zirconia from its vapor phase onto zirconia and nickel oxide phases of the s...
Saved in:
Personal Name(s): | Vasylyev, Olexsandr |
---|---|
Brychevskyi, Mykola / Brodnikovskyi, Iegor / Firstov, Sergiy / Andrzejczuk, Mariusz / Spychalski, Maciek / Lewandowska, Malgorzata / Kurzydlowski, Krzysztof Jan / Steinberger-Wilckens, Robert / Mertens, Josef / Malzbender, Jürgen | |
Contributing Institute: |
Werkstoffstruktur und -eigenschaften; IEK-2 Grundlagen der Elektrochemie; IEK-9 |
Published in: | Advances in Ceramic Science and Engineering, 3 (2014) 2014, S. 25-35 |
Imprint: |
Riley, Ind.
Science and Engineering Publishing Company (SEP)
2014
|
Document Type: |
Journal Article |
Research Program: |
Renewable Energies Fuel Cells |
Publikationsportal JuSER |
The structure of the transitional zone between a zirconia film deposited by EB-PVD and its porous NiO-ZrO2 substrate were studied using transmission and scanning electron microscopy. The plausible condensation mechanisms of zirconia from its vapor phase onto zirconia and nickel oxide phases of the substrate were established. The condensation of zirconia was identified as a two-stage process with two mechanisms of growth, planar and cellular, similar to solidification from the liquid phase. ZrO2 condensation on ZrO2 and NiO phases occurs with different routes. During the planar growth on the ZrO2, the ZrO2 film nucleates and grows up to ~0.3-0.5 μm with no orientation preference as continuous "layer by layer" defective film. The planar ZrO2 film on the NiO of ~0.5-0.7 μm thickness is discontinuous and porous; it consists of oriented structurally perfect "islands". The differences found are probably the result of differences in the melting temperature of ZrO2 and NiO, and Zr and Ni affinities to oxygen as well as their different behavior under high vacuum. The deposition affected zone surrounding the ZrO2 nucleation site is established.Keywords: Zirconia Film; Nucleation Mechanism; Growth Mechanism; Thin Structure; Solid Oxide Fuel Cell; Electron Beam – Physical Vapor Deposition |