Laser annealing of BST thin films with reduced cracking at an elevated temperature
Laser annealing of BST thin films with reduced cracking at an elevated temperature
An excimer laser (KrF, 248 nm) was used to crystallize barium strontium titanate thin films of thickness 95 nm. Numerical simulation was first performed to get an idea about the laser energy suitable for crystallization. Amorphous films deposited by chemical solution deposition were irradiated at di...
Saved in:
Personal Name(s): | Halder, S. |
---|---|
Boettger, U. / Schneller, T. / Waser, R. / Baldus, O. / Jacobs, P. / Wehner, M. | |
Contributing Institute: |
Elektronische Materialien; IFF-IEM JARA-FIT; JARA-FIT Center of Nanoelectronic Systems for Information Technology; CNI |
Published in: | Materials science and engineering / B, 133 (2006) |
Imprint: |
New York, NY [u.a.]
Elsevier
2006
|
DOI: |
10.1016/j.mseb.2006.06.003 |
Document Type: |
Journal Article |
Research Program: |
Grundlagen für zukünftige Informationstechnologien |
Series Title: |
Materials Science and Engineering B
133 |
Subject (ZB): | |
Publikationsportal JuSER |
An excimer laser (KrF, 248 nm) was used to crystallize barium strontium titanate thin films of thickness 95 nm. Numerical simulation was first performed to get an idea about the laser energy suitable for crystallization. Amorphous films deposited by chemical solution deposition were irradiated at different energies with different frequencies (40-150 Hz), laser fluences (100-150 mJ/cm(2)) and pulses (400-1000) while maintaining the substrate at 25 and 250 degrees C. Films were found to crystallize above 100 mJ/cm(2) in both cases. Films crystallized with substrate temperatures of 250 degrees C were noticed to have less cracks. The microstructure of these films were analyzed with a scanning electron microscope. From the XPS analysis, it is inferred that the top few nanometers have a different structure compared to normal furnace annealed thin films. This top surface layer was found to be dependent on the laser energy used for crystallization. The dielectric constant was found to increase from 60 to 180 for the 95 nm thin films on increasing the laser fluence. Films crystallized with 120mJ/cm(2) while maintaining a substrate temperature of 250 degrees C have leakage current densities of 1 x 10(-7) A/cm(2) at 1.5 V and a dielectric constant of 200. (c) 2006 Elsevier B.V. All rights reserved. |