Survey of Zirconium‐Containing NaSICON‐type Solid‐State Li+ Ion Conductors with the Aim of Increasing Reduction Stability by Partial Cation Substitution
Survey of Zirconium‐Containing NaSICON‐type Solid‐State Li+ Ion Conductors with the Aim of Increasing Reduction Stability by Partial Cation Substitution
Various compositions of the series Li1+xM3+xZr2−x(PO4)3 where M3+=Al3+, Sc3+, Y3+ were prepared by solution-assisted solid-state reaction, since they could have a higher reduction stability as solid electrolytes in lithium batteries than in germanium- or titanium-containing materials. The influence...
Saved in:
Personal Name(s): | Loutati, Asmaa (Corresponding author) |
---|---|
Odenwald, Philipp / Aktekin, Burak / Sann, Joachim / Guillon, Olivier / Tietz, Frank (Corresponding author) / Fattakhova-Rohlfing, Dina | |
Contributing Institute: |
Helmholtz-Institut Münster Ionenleiter für Energiespeicher; IEK-12 Werkstoffsynthese und Herstellungsverfahren; IEK-1 |
Published in: | Batteries & supercaps, 5 (2022) 11, S. e202200327 |
Imprint: |
Weinheim
Wiley-VCH
2022
|
DOI: |
10.1002/batt.202200327 |
Document Type: |
Journal Article |
Research Program: |
Fundamentals and Materials |
Link: |
Get full text OpenAccess |
Publikationsportal JuSER |
Please use the identifier: http://hdl.handle.net/2128/33029 in citations.
Various compositions of the series Li1+xM3+xZr2−x(PO4)3 where M3+=Al3+, Sc3+, Y3+ were prepared by solution-assisted solid-state reaction, since they could have a higher reduction stability as solid electrolytes in lithium batteries than in germanium- or titanium-containing materials. The influence of substitution on crystallographic parameters, density, and ionic conductivity were investigated. The cation substitution of M3+ (M=Al, Sc, Y) for Zr4+ in LiZr2(PO4)3 stabilizes the rhombohedral NaSICON structure (space group urn:x-wiley:25666223:media:batt202200327:batt202200327-math-0001 ) at room temperature and increases the ionic conductivity significantly. Here, at 25 °C and with a consistent relative density of 94 %–96 %, an ionic conductivity of 2.7×10−5 S cm−1, 6.7×10−5 S cm−1, and 3.6×10−6 S cm−1 was achieved with the compositions Li1.2Sc0.2Zr1.8(PO4)3, Li1.2Y0.2Zr1.8(PO4)3, and Li1.2Al0.2Zr1.8(PO4)3, respectively. In comparison with Li1+xScxZr2−x(PO4)3, the Y3+ substitution in LiZr2(PO4)3 enhanced the ionic conductivity slightly and denoted the maximum Li+ ionic conductivity obtained at room temperature. However, substitution with Al3+ decreased the ionic conductivity. For the first time, this work provides a complete overview of three series of solid Li-ion conductors in the Li2O-M2O3-ZrO2-P2O5 system where M=Al, Sc, Y. Noticeable differences in the chemistry of resulting compounds were observed, which likely depend on the ionic radius of the cations being substituted. The series with Sc showed complete miscibility from x=0 to x=2 with a continuous change of the NaSICON polymorphs. The series with Y showed a solubility limit at about x=0.3 and higher substitution levels led to the increasing formation of YPO4. The series with Al exhibited continuously decreasing ionic conductivity until x=1, whereupon the investigation was terminated due to its very low conductivity of about 10−10 S cm−1. |