Ternary Al-Pd-Co monoclinic phases
Ternary Al-Pd-Co monoclinic phases
The ternary Al-Pd-Co V-phase and U-phase (reported previously) were studied by powder X-ray and electron diffraction. The V-phase was found to have a primitive monoclinic structure [a=1.0068(2) nm, b=0.3755(1) nm, c=0.6512(4) nm and beta =102.38(6)degrees for Al70.0Pd9.2Co20.8]. The U-phase was foun...
Saved in:
Personal Name(s): | Mi, S. |
---|---|
Yurechko, M. / Wu, J. / Grushko, B. | |
Contributing Institute: |
Mikrostrukturforschung; IFF-IMF |
Published in: | Journal of alloys and compounds, 329 (2002) S. L1 - L4 |
Imprint: |
Lausanne
Elsevier
2002
|
Physical Description: |
L1 - L4 |
DOI: |
10.1016/S0925-8388(01)01355-X |
Document Type: |
Journal Article |
Research Program: |
Kondensierte Materie |
Series Title: |
Journal of Alloys and Compounds
329 |
Subject (ZB): | |
Publikationsportal JuSER |
The ternary Al-Pd-Co V-phase and U-phase (reported previously) were studied by powder X-ray and electron diffraction. The V-phase was found to have a primitive monoclinic structure [a=1.0068(2) nm, b=0.3755(1) nm, c=0.6512(4) nm and beta =102.38(6)degrees for Al70.0Pd9.2Co20.8]. The U-phase was found to have a C-centered monoclinic structure [a= 1.9024(4) nm, b=2.9000(4) nm, c= 1.3140(4) nm; beta =117.26(3)degrees for Al69.1Pd16.5Co14.1]. (C) 2001 Elsevier Science BY All rights reserved. |