Investigation of the primary crystallization of Ni-17 at.% P alloy by ASAXS
Investigation of the primary crystallization of Ni-17 at.% P alloy by ASAXS
Primary crystallization of Ni(P) particles in hypoeutectic Ni - P amorphous alloy obtained by electroless deposition has been investigated with ASAXS. The particle size distribution, the size dependence of the particle composition and the amorphous matrix composition were found simultaneously. The s...
Saved in:
Personal Name(s): | Tatchev, D. |
---|---|
Goerigk, G. / Valova, M. J. / Dille, J. / Kranold, R. / Armyanov, S. / Delplancke, J.-L. | |
Contributing Institute: |
JCNS; JCNS Neutronenstreuung; IFF-INS Streumethoden; IFF-ISM |
Published in: | Journal of applied crystallography, 38 (2005) S. 787 - 794 |
Imprint: |
Copenhagen
Munksgaard
2005
|
Physical Description: |
787 - 794 |
DOI: |
10.1107/S0021889805024489 |
Document Type: |
Journal Article |
Research Program: |
Kondensierte Materie |
Series Title: |
Journal of Applied Crystallography
38 |
Subject (ZB): | |
Link: |
Get full text OpenAccess |
Publikationsportal JuSER |
Please use the identifier: http://dx.doi.org/10.1107/S0021889805024489 in citations.
Primary crystallization of Ni(P) particles in hypoeutectic Ni - P amorphous alloy obtained by electroless deposition has been investigated with ASAXS. The particle size distribution, the size dependence of the particle composition and the amorphous matrix composition were found simultaneously. The size distribution consists of a peak at particle radius of similar to 1 nm and a tail spanning from similar to 2 to 15 nm. The composition of the particles of the peak changes from similar to 14 to similar to 2 at.% P as their radius grows from 0.7 to about 3 nm. The particles in the tail of the size distribution ( 2 - 15 nm) have nearly constant P content in the range of 0 - 2 at.%. The matrix composition tends to the eutectic one at the end of the primary crystallization process. |